Magnetic Field-Induced Strain of Metamagnetic Heusler Alloy Ni41Co9Mn31.5Ga18.5

Abstract

Ni41Co9Mn31.5Ga18.5 is a re-entrant and metamagnetic Heusler alloy. In order to investigate the magnetic functionality of polycrystalline Ni41Co9Mn31.5Ga18.5, magnetic field-induced strain (MFIS) measurements were performed. A 0.12% MFIS was observed at 340 K and 10 T. Strict MFISs between 330 and 370 K were observed. These magneto-structural variances acted in concert with the metamagnetic property observed by the magnetization measurements and magneto-caloric property observed by the caloric measurements in applied magnetic fields. The MFISs were proportional to the fourth power of the magnetization, and this result is in agreement with Takahashi’s spin fluctuation theory of itinerant electron magnetism. The investigation of time response of the MFIS was performed by means of water-cooled electric magnet, zero magnetic field to 1.66 T in 8.0 s at 354 K. A 2.2×10−4 MFIS was observed, which was 80% of the MFIS in a 60-s mode. This indicates that a high-speed transition has occurred on applying magnetic fields